Título :	Vida à fadiga da liga de alumínio Al7075 - T6511 na presença de defeitos por indentação
Autor :	Silva, Vinícius Rodrigues Moraes
Orientador(es)::	Mamiya, Edgar Nobuo
Assunto::	Fadiga Defeitos por indentação Ligas de alumínio
Fecha de publicación :	17-dic-2020
Data de defesa::	30-jul-2020
Citación :	SILVA, Vinícius Rodrigues Moraes. Vida à fadiga da liga de alumínio Al7075 - T6511 na presença de defeitos por indentação. 2020. [77] f. il. Dissertação (Mestrado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2020.
Abstract:	This work investigates fatigue life of the aluminum alloy 7075-T6511 under the presence of defects produced by indentations. The material was subjected to fully reversed tractioncompression cyclic loads with nominal stress amplitudes between 190 MPa and 450 MPa, resulting in lives of 4 × 103 to 107 cycles. Indentation defects --- produced with loads of 62.5 kgf, 31.3 kgf and 15.6 kgf --- caused fatigue life reductions of up to 82 times for the stress amplitudes considered. From the obtained S-N curves, the stress amplitudes corresponding to a life of 107 cycles were estimated, comparing them with the fatigue strength obtained through the Murakami and Endo model. It was observed that the fatigue strength estimates thus obtained were conservative when compared with the Murakami and Endo model, presenting a difference of 17.0% for the case of defects with 62.5 kgf indentation force and 6.8% for 31.3 kgf indentation force defects. Under 62.5 kgf and 31.3 kgf indentation forces defects, the river marks indicate that the cracks started close to the edge of the defect. In the case of 15.6 kgf indentation force, the defect did not determine the crack initiation site nor the fatigue life. A numerical study was carried out using the finite element method, in which the indentation and a loading cycle were simulated. The Smith, Watson and Topper parameter was considered to estimate the life of the material, based on the numerical results obtained. The SWT parameter is critical in the region where the river marks indicate the crack initiation. This parameter estimated a life of 30,000 cycles, while a life of 200,000 cycles was experimentally obtained, which represents a difference of 6.7 times. On the other hand, the disregard of the defect leads to a life estimate about 67 times greater than that observed experimentally. Thus, compared to the life estimate without considering the defect, the SWT parameter was more precise and, even more importantly, it produced a conservative life estimate.
metadata.dc.description.unidade:	Faculdade de Tecnologia (FT) Departamento de Engenharia Mecânica (FT ENM)
Descripción :	Dissertação (Mestrado em Ciências Mecânicas)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, Brasília, 2020.
metadata.dc.description.ppg:	Programa de Pós-Graduação em Ciências Mecânicas
Licença::	A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data.
Aparece en las colecciones:	Teses, dissertações e produtos pós-doutorado

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.