Título:	Avaliação das propriedades físicas, químicas e adesivas de materiais restauradores do tipo Alcasite
Autor(es):	González, José Alejandro Castro
Orientador(es):	Zanatta, Rayssa Ferreira
Assunto:	Alcasite (Odontologia) Bioatividade Restauração (Odontologia) Alcasite (Odontologia) - propriedades
Data de publicação:	25-Set-2024
Data de defesa:	27-Mai-2024
Referência:	GONZÁLEZ, José Alejandro Castro. Avaliação das propriedades físicas, químicas e adesivas de materiais restauradores do tipo Alcasite. 2024. 61 f., il. Dissertação (Mestrado em Odontologia) — Universidade de Brasília, Brasília, 2024.
Abstract:	Restorative materials with bioactive characteristics have appeared on the market with the promise of improving the remineralization processes of the tooth structure and slowing down demineralization. Incorporating different glass particles into resins or composites has offered different characteristics in terms of these materials' adhesion, viscosity, and physical and chemical resistance and expanded their use in various clinical situations. In this context, alkasite-type materials are a recent option for restorative use, containing bioactive properties. This work aimed to evaluate the chemical and mechanical behavior of alkasite materials under different aging protocols and compare them with other conventional materials, with or without bioactivity. This text provides a brief review of the topic in chapter 1. In the second chapter, the flexural strength, microhardness, sorption, and solubility of the following materials were evaluated: Alkasite (Cention N, Ivoclar), Resin modified glass ionomer cement (Riva LC, SDI), Bioactive composite resin (Beautifill II, Shofu), and conventional composite resin (Z100, 3M ESPE). The analyses were carried out under three aging conditions: control (no aging), thermocycling (5000 cycles, 5º-55ºC, 30 s), and erosive challenge (citric acid, pH 3.6, 4x day, 5 days). The results of the study indicate that the aging carried out significantly impacted the flexural strength, microhardness, sorption, and solubility of the materials evaluated. Finally, the third and final chapter presents the evaluation of the adhesive resistance to microshear of different bioactive materials, both in enamel and dentin. The following were evaluated: Alkasite (Cention N, Ivoclar) applied with universal adhesive; Alkasite (Cention N, Ivoclar) applied without adhesive; Resin modified glass ionomer cement (Riva LC, SDI); and Bioactive self-adhesive composite resin (Stella, SDI). The comparison was made after thermocycling and erosive cycling. It was observed that the materials tended to have better bonding resistance to erosive aging and the chemical adhesion capacity of the materials (use without adhesive) had a great impact on the number of pre-test failures. Presentation of results and discussion of findings are provided in each chapter.
Unidade Acadêmica:	Faculdade de Ciências da Saúde (FS)
Informações adicionais:	Dissertação (mestrado) — Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em em Odontologia, 2024.
Programa de pós-graduação:	Programa de Pós-Graduação em Odontologia
Licença:	A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.unb.br, www.ibict.br, www.ndltd.org sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra supracitada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data.
Aparece nas coleções:	Teses, dissertações e produtos pós-doutorado

Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.